Hastelloy Plates

AMS 5774 Wire

AMS 5774 Wire, is produced by special lubricant free, roller die forming followed by surface abrasion & cleaning processes. It is a nitrogen strengthened hardenable stainless alloy with austenitic or martensitic structure depending on thermal cycle. 

Chemical Composition
  • Carbon; 0.08-0.12
  • Manganese; 0.50-1.25
  • Silicon; 0.50max
  • Sulfur; 0.030max
  • Phosphorus; 0.040max
  • Chromium; 16.0-17.0
  • Nickel; 4.0-5.0
  • Molybdenum; 2.50-3.25
  • Nitrogen; 0.07-0.13
  • Iron; Bal

AMS 5743 Bar

AMS 5743, is a chromium nickel molybdenum stainless steel. It is a heat treatable austenitic/ martensitic alloy. The properties of AMS 5743 are that of strength of a heat treatable martensitic grades with the corrosion resistance of some of the chromium nickel austenitic grades.

Chemical Composition
Carbon; 0.10-0.15
Phosphorus; 0.040max
Silicon; 0.50max
Nickel; 4.0-5.0
Nitrogen; 0.07-0.13
Manganese; 0.50-1.25
Sulfur; 0.030max
Chromium; 15.0-16.0
Molybdenum; 2.5-3.25
Iron; Bal 

Mechanical Properties
0.2% Yield Strength; 979Mpa
Ultimate Tensile Strength; 1489Mpa
Elongation in2" ; 19%

AMS-5780 Wire

AMS-5780, is a corrosion & heat resistant steel. It is manufactured by special lubricant free, roller-die forming followed by surface abrasion & cleanning processes. Its manufacturing processes ensure consistent metallurgical integrity of the alloy with regard to purity of the welding wire surface.

Chemical Composition
  • Carbon; 0.10-0.15
  • Manganese; 0.50-1.25
  • Silicon; 0.50max
  • Sulfur; 0.030max
  • Phosphorus; 0.040max
  • Chromium; 15.0-16.0
  • Nickel; 4.0-5.0
  • Molybdenum; 2.50-3.25
  • Nitrogen; 0.07-0.13
  • Copper; 0.50max
  • Iron; Balance

AMS-5840 Bar

AMS-5840, is typically used as a filler metal for gas tungsten arc & gas metal arc welding of steel of similar composition requiring joints with strength & corrosion resistance comparable to those of the base metal.

Chemical Composition
  • Carbon; 0.050max
  • Phosphorous; 0.0080max
  • Manganese; 0.10max
  • Silicon; 0.10max
  • Sulfur; 0.010max
  • Chromium; 12.9
  • Hydrogen; 0.0025max
  • Molybdenum; 2.25
  • Nitrogen; 0.010max
  • Oxygen; 0.0050max
  • Aluminium; 1.10
  • Nickel; 8.0max
  • Iron; 76

AMS-5659 Bar/ Wire

AMS-5659, is a high strength precipitation hardening stainless steel, most applications are in aerospace & other high technology industry.

Chemical Composition
  • Carbon; 0.07max
  • Manganese; 1.00max
  • Phosphorus; 0.030max
  • Chromium; 14.0-15.50
  • Copper; 2.50-4.50
  • Silicon; 1.00max
  • Molybdenum; 0.50max
  • Niobium+Columbium; 0.45max
  • Sulfur; 0.02max
  • Nickel; 3.50-5.50
  • Iron; Bal

Mechanical Properties
  • Proof Stress; 700-1170Mpa
  • Tensile Strength; 930-1310Mpa
  • Elongation; 10-16%
  • Hardness Brinell; 277-444HB

AMS-5812 Bar

AMS-5812 Bar/ Wire

AMS-5622 Bar

AMS-5622 Bar/ Wire

AMS 5643 Bar and Wire

We are involved in offering a wide range of AMS 5643 Bar/Wire.


Chemical Composition
Carbon; 0.07max
Silicon; 1.0max
Manganese; 1.0max
Phosphorus; 0.040max
Sulfur; 0.030max
Chromium; 15.0-17.5
Nickel; 3.0-5.0
Copper; 3.0-5.0

Mechanical Properties
Tensile Strength; 190ksi
0.2% Yield Strength; 170ksi
Elongation; 10%
Hardness Rockwell; 388-444

AMS 5825 Bar

AMS 5825 Bar/Wire
AMS 5825, is the most widely used steel of the precipitation hardening grade steel. It has high toughness, strength & corrosion resistance. It is used for applications such as aircraft & gas turbines, chemical process components, paper mills, nuclear reactor & oil field.

Chemical Composition
  • Carbon; 0.05max
  • Manganese; 0.25-0.75
  • Silicon; 0.75max
  • Sulfur; 0.025max
  • Phosphorus; 0.025max
  • Chromium; 16.0-16.75
  • Nickel; 4.50-5.00
  • Columbium; 0.15-0.30
  • Copper; 0.15-0.30
  • Molybdenum; 0.75max
  • Iron; Bal

AMS 5678 Bar

AMS 5678 Bar/Wire
AMS 5678, is a hardenable chromium nickel aluminium stainless steel combining high strength & moderate corrosion resistance. It is used for application requiring good strength, corrosion resistance & mechanical properties up to 800F in service. 

Chemical Composition
  • Carbon; 0.09max
  • Phosphorus; 0.040max
  • Sulphur; 0.040max
  • Manganese; 1.00max
  • Chromium; 16.0-18.0
  • Silicon; 1.00max
  • Aluminium; 0.75-1.50
  • Nickel; 6.5-7.75
  • Iron; Bal

AMS 5656 Bar

AMS 5656 Bar/Wire
AMS 5656, is a high manganese nitrogen strengthened stainless steel. It includes high strength in the annealed condition, excellent resistance to corrosion at high temperature. It is used for numerous applications such as chemical processing, pollution control equipment & aircraft engine components.

Chemical Composition
  • Carbon; 0.040max
  • Phosphorus; 0.060max
  • Silicon; 1.00max
  • Nickel; 5.5-7.5
  • Iron; Bal
  • Manganese; 8.0-10.0
  • Sulfur; 0.030max
  • Chromium; 19.0-21.5
  • Nitrogen; 0.15-0.40
  • Molybdenum; 0.75max
  • Copper; 0.75max

Mechanical Properties
  • 0.2% Yield Strength; 62ksi, 428Mpa
  • Tensile Strength; 95ksi, 655Mpa
  • Elongation in 2" ; 46% 

AMS 5636 Bar

AMS 5636 Bar/Wire, is an austenitic, non magnetic, extremely tough & dutile. It is one of the more common chrome nickel stainless & heat resisting steel. Cold working dramatically increase its hardness & applications range from the stamping, spinning & wire forming industry to food & beverage, sanitary, cryogenic & pressure containing.

Chemical Composition
  • Carbon; 0.15max
  • Sulfur; 0.030max
  • Silicon; 1.00max
  • Phosphorus; 0.045max 
  • Manganese; 2.00max
  • Chromium; 17.0-19.0
  • Nickel; 8.0-10.0

Mechanical Properties
  • Tensile Strength; 620Ma, 89900psi
  • 0.2% Yield Strength; 275Mpa, 39900psi
  • Elongation(in 50mm); 55%
  • Hardness, Brinell; 147

AMS 5637 Bar

AMS 5637 Bar/Wire
AMS 5637, is used for defense, aerospace, oil & gas, wind turbine, pipeline, shipbuilding, medical instrument, satellite & rocket building. 

Chemical Composition 
  • Chromium; 17.0-19.0
  • Nickel; 8.0-10.0
  • Manganese; 2.00max
  • Silicon; 1.00max 
  • Carbon; 0.15max
  • Sulfur; 0.030max 
  • Phosphorus; 0.045max

Mechanical Properties
  • Tensile Strength; 620Mpa, 89900psi
  • 0.2% Yield Strength; 275Mpa, 39900psi
  • Elongation(in 50mm); 55%
  • Hardness, Rockwell B; 85

AMS 5688 Bar

AMS 5688 Bar/Wire
AMS 5688, is typicaly used for applications such as engineered components, springs, wire cloth & mesh, hose braiding etc.

Chemical Composition
  • Carbon; 0.12max
  • Manganese; 2.00max
  • Phosphorus; 0.045max
  • Sulfur; 0.030max
  • Silicon; 1.00max
  • Chromium; 17.0-19.0
  • Nickel; 8.0-10.0
  • Iron; Bal

AMS-5546 Sheet

AMS-5546 Sheet/Strip is a columbium/tantalum stabilised austenitic chromium nickel stainless steel. This material is stabilised against formation by the addition of columbium & tantalum. Its applications are furnace heating elements, cabin heaters, aircraft exhaust & heavy wall welded equipment.

Chemical Composition
  • Carbon; 0.08max
  • Manganese; 2.00max
  • Phosphorus; 0.045max
  • Sulfur; 0.030max
  • Silicon; 0.75max
  • Chromium; 17.0-19.0
  • Nickel; 9.0-13.0
  • Columbium+Tantalum; 10xCmin to 1.00max
  • Iron; Bal 

Mechanical Properties
  • 0.2% Yield Strength Offset; 30,000psi, 205Mpa
  • Tensile Strength; 75,000psi, 515Mpa
  • Elongation in 2" ; 40%

AMS-5547 Sheet

AMS-5547, is a chromium nickel molybdenum stainless steel. It is a heat treatable martensitic alloy. It is used for industrial cutters, knives, blades, shafts, disc & similar parts where high strength is required at intermediate elevated temperature.

Chemical Composition
  • Carbon; 0.10-0.15
  • Phosphorus; 0.040max
  • Silicon; 0.50max
  • Nickel; 4.0-5.0
  • Nitrogen; 0.07-0.13
  • Manganese; 0.50-1.25
  • Sulfur; 0.030max
  • Chromium; 15.0-16.0
  • Molybdenum; 2.5-3.25
  • Iron; Bal

Mechanical Properties
  • Yield Strength 0.2% Strength Offset; 979Mpa
  • Tensile Strength; 1255Mpa
  • Elongation in 2"; 19%
  • Reduction of Area; 38%
  • Rockwell C Hardness; 48

AMS-5604 Sheet

AMS-5604 Sheet/ Plate/ Strip
AMS-5604, is a martensitic, precipitation hardening stainless steel that provides an outstanding combination of high strength & hardness along with excellent corrosion resistance. It is a versatile material widely used in the paper & pulp, aerospace, chemical, petrochemical, food processing industries. 

Chemical Composition
  • Carbon; 0.07max
  • Silicon; 1.00max
  • Manganese; 1.00max
  • Phosphorus; 0.040max
  • Sulfur; 0.030max
  • Chromium; 15.0-17.5
  • Nickel; 3.0-5.0
  • Cb+Ta; 5XC/0.45
  • Copper; 3.0-5.0

Mechanical Properties
  • Tensile Strength; 190ksi
  • 0.2% Yield Strength; 170ksi
  • Rockwell C Hardness; 40-47 

AMS 5528 Sheet

AMS 5528 Sheet/ Plate/ Strip
AMS 5528 is a precipitation hardened stainless steel that is well suited for aerospace & other applications requiring high strength & good corrosion resistance & formability.

Chemical Composition
  • Carbon; 0.09max
  • Manganese; 1.00max
  • Phosphorus; 0.05max
  • Sulfur; 0.03max
  • Silicon; 1.00max
  • Chromium; 16.0-18.0
  • Nickel; 6.75-7.75
  • Aluminium; 0.75-1.50

Mechanical Properties
  • Tensile Strength; 130000psi, 896Mpa
  • 0.2% Tensile Strength; 40000psi, 276Mpa
  • Elongation % in 2"; 35  
  • Hardness Rockwell; B85

AMS-5529 Sheet

AMS-5529 Sheet/ Strip
AMS-5529 Sheet/ Strip, is a semi austenitic stainless steel which is austenitic in the annealed condition. It provides high strength & hardness, excellent fatigue properties, good corrosion resistance & minimum distortion upon heat treatment. 

Chemical Composition
  • Carbon; 0.090max
  • Manganese; 1.00max
  • Silicon; 1.00max
  • Chromium; 16.0-18.0
  • Nickel; 6.50-7.75
  • Aluminium; 0.75-1.50
  • Phosphorus; 0.040max
  • Sulfur; 0.030max
  • Iron; Bal
Mechanical Properties
  • Tensile Strength(max); 150ksi, 1035Mpa
  • 0.2% Offset Yield Strength(max); 65ksi, 450Mpa

AMS 5595 Sheet

AMS-5595, is a high manganese nitrogen strengthened steel. It properties include high strength in the annealed condition. It has excellent resistance to corrosion at high temperatures. It is used in a numerous applications including chemical processing, aircraft engine & pollution control equipment.

Chemical Composition
  • Carbon; 0.040max
  • Phosphorus; 0.060max
  • Silicon; 1.00max
  • Nickel; 5.5-7.5
  • Manganese; 8.0-10.0
  • Sulfur; 0.030max
  • Chromium; 19.0-21.5
  • Nitrogen; 0.15-0.40
  • Molybdenum; 0.75max
  • Copper; 0.75max
  • Iron; Bal

Mechanical Properties
  • 0.2% Yield Strength; 62ksi, 428Mpa
  • Ultimate Tensile Strength; 95ksi, 655Mpa
  • Elongation in 2"; 46%

AMS 5901 Sheet

AMS 5901 Sheet Strip
AMS 5901, contains 17% chromium & 7% nickel austenitic stainless steel. It has good resistance to atmosphere corrosion & its bright attractive surface make it an excellent choice for decorative structural applications.

Chemical Composition
  • Carbon; 0.15max
  • Silicon; 1.00max
  • Manganese; 2.00max
  • Phosphorus; 0.040max
  • Sulfur; 0.030max
  • Chromium; 16.0-18.0
  • Nickel; 6.0-8.0
  • Copper; 0.75max
  • Molybdenum; 0.75max
  • Iron; Bal

Mechanical Properties
  • Tensile Strength(min): 75ksi, 515Mpa
  • 0.2% Yield Strength(min); 30ksi, 205Mpa
  • Elongation % in 2"; 40%
  • Hardness HRC; 92

AMS 5517(1/4HD) Sheet/ Strip

AMS 5518(1/2HD) Sheet/ Strip

AMS 5902(3/4HD) Sheet/ Strip

AMS 5519(FH) Sheet/ Strip

AMS 5516 Sheet

AMS 5516 Sheet/ Plate
AMS 5516, is an extremely tough, ductile grade that demonstrates superior corrosion resistance. It is non magnetic grade that is not hardenable by heat treatment. 
Chemical Composition
  • Carbon; 0.15max
  • Manganese; 2.00max
  • Phosphorus; 0.045max 
  • Sulfur; 0.030max
  • Silicon; 0.75max
  • Chromium; 17.0-19.0
  • Nickel; 8.0-10.0
  • Aluminium; 0.10max

Mechanical Properties
  • 0.2% Offset Yield Strength; 30000psi, 205Mpa
  • Tensile Strength; 75000psi, 515Mpa
  • Elongation in 2"; 40% 

AMS 5903(1/4HD) Sheet/ Strip

AMS 5904(1/2HD) Sheet/ Strip

AMS 5905(3/4HD) Sheet/ Strip

AMS 5906(FH) Sheet/ Strip

AMS 5549 Plate

AMS 5549, is a chromium nickel molybdenum stainless steel. It is a heat treatable austenitic alloy. It is used for industrial cutters, blades, discs, rotors, shafts, knives etc.

Chemical Composition
  • Carbon; 0.10-0.15
  • Phosphorus; 0.040max
  • Manganese; 0.5-1.25
  • Chromium; 15.0-16.0
  • Silicon; 0.50max
  • Sulfur; 0.030max
  • Molybdenum; 2.5-3.5
  • Nickel; 4.0-5.0
  • Iron; 73.53-77.33

AMS-5864 Plate

AMS-5864, is a martensitic precipitation hardening stainless steel that has excellent strength, high hardness, good corrosion resistance & superior toughness. It offers a high level of useful mechanical properties under severe environmental conditions.

Chemical Composition
  • Carbon; 0.05max
  • Phosphorus; 0.010max
  • Silicon; 0.10max
  • Nickel; 7.5-8.5
  • Aluminium; 0.90-1.35
  • Iron; Bal
  • Manganese; 0.10max
  • Sulfur; 0.008max
  • Chromium; 12.25-13.25
  • Molybdenum; 2.0-2.5
  • Nitrogen; 0.01max

Mechanical Properties
  • Tensile Strength; 220ksi
  • 0.2% Yield Strength; 205ksi
  • Elongation; 10%
  • Reduction of Area; 45%
  • Rockwell C Hardness; 45

AMS 5862 Sheet

AMS 5862 Sheet/ Plate/ Strip
AMS 5862, is a precipitation hardening alloy exhibiting high strength & hardness with moderate corrosion resistance. It is designed to have greater toughness especially in the through thickness direction. It is used in applications that require high transverse strength & toughness such as nuclear reactor components, engine parts, aircraft components etc.

Chemical Composition
  • Carbon; 0.07
  • Silicon; 1.00max
  • Manganese; 1.00max
  • Phosphorus; 0.030max
  • Sulfur; 0.015max
  • Chromium; 14.0-15.50
  • Nickel; 3.50-4.50
  • Copper; 2.50-4.50
  • Cobalt; 0.45max
  • Iron; Bal
  • Molybdenum; 0.50max

Mechanical Properties
  • Tensile Strength; 190ksi
  • 0.2% Yield Strength; 170ksi
  • Rockwell C Hardness; 38max

AMS-5520 Sheet

AMS-5520 Sheet/ Plate/ Strip
AMS-5520, is a precipitation hardening stainless steel used for applications requiring high strength & moderate corrosion resistance.

Chemical Composition
  • Carbon; 0.09max
  • Manganese; 1.00max
  • Silicon; 1.00max
  • Phosphorus; 0.040max
  • Sulfur; 0.030max
  • Chromium; 14.0-16.0
  • Nickel; 6.50-7.75
  • Molybdenum; 2.0-3.0
  • Aluminium; 0.75-1.50
Mechanical Properties
  • Tensile Strength, max; 190ksi
  • Yield Strength, max; 170ksi
  • Elongation; 4%
  • Hardness; 40HRC

AMS 5513 Plate

AMS 5513, has higher chromium & lower carbon content. Lower carbon minimizes chromium carbide precipitation due to welding & its susceptibility to intergranular corrosion. 

Chemical Composition
  • Carbon; 0.08max
  • Silicon; 1.00max
  • Manganese; 2.00max
  • Phosphorus; 0.040max
  • Sulfur; 0.030max
  • Chromium; 18.0-20.0
  • Nickel; 8.0-10.5
  • Iron; Bal
  • Molybdenum; 0.75max
  • Copper; 0.75max

Mechanical Properties
  • Tensile Strength(ksi); 75min
  • Yield Strength(ksi); 30
  • Elongation; 40%
  • Hardness; 202HB

AMS 5515 Plate

AMS 5515 is non hardenable by heat treatment & in non magnetic in the annealed condition. It becomes slightly magnetic witgh cold working.  

Chemical Composition
  • Carbon; 0.08-0.15
  • Manganese; 2.00max
  • Silicon; 1.00max
  • Chromium; 17.0-19.0
  • Nickel; 7.0-10.0
  • Molybdenum; 0.75max
  • Phosphorus; 0.040max
  • Sulfur; 0.030max
  • Iron; Bal

Mechanical Properties
  • Tensile Strength, min; 75ksi, 515Mpa
  • 0.2% Offset Yield Strength, min; 30ksi, 205Mpa
  • Elongation; 40%min

AMS 5622 Tube

AMS 5622, is one of the most widely used precipitation hardening grades. It provides good corrosion resistance, high hardness, strength & toughness.

Chemical Composition
  • Carbon; 0.07max
  • Silicon; 1.00max
  • Manganese; 1.00max
  • Phosphorus; 0.040max
  • Sulfur; 0.030max
  • Chromium; 15.0-17.50
  • Molybdenum; 0.50max
  • Nickel; 3.0-5.0
  • Columbium; 0.45max
  • Copper; 3.0-5.0
  • Iron; Bal

Mechanical Properties
  • 0.2% Proof Stress; 1172Mpa(min)
  • Tensile Strength; 1310Mpa(min)
  • Elongation; 6-10%

AMS 5643 Tube

AMS 5643 Tube, is used for high strength & corrosion resistance. It is used for applications where high fatigue strength, good resistance is useful. 

Chemical Composition
  • Carbon; 0.07max
  • Manganese; 1.00max
  • Phosphorus; 0.040max
  • Sulfur; 0.030max
  • Silicon; 1.00max
  • Chromium; 15.0-17.50
  • Nickel; 3.0-5.0
  • Copper; 3.0-5.0
  • Molybdenum; 0.50max

Mechanical Properties
  • Tensile Strength; 1310Mpa
  • 0.2% Proof Stress; 1172Mpa
  • Hardness(HB); 388-444